The manufacture of prefabricated building materials containing binding products such as ettringite (6CaO•Al2O3•3SO3•32H2O) and calcium silicate hydrate (CSH) can give, in addition to other well-defined industrial activities, the opportunity of using wastes and by-products as raw materials, thus contributing to further saving of natural resources and protection of the environment. Two ternary mixtures, composed by 40% flue gas desulfurization (FGD) gypsum or natural gypsum (as a reference material), 35% calcium hydroxide and 25% coal fly ash, were submitted to laboratory hydrothermal treatments carried out within time and temperature ranges of 2 hours–7 days and 55°-85°C, respectively. The formation of (i) ettringite, by hydration of calcium sulfate given by FGD or natural gypsum, alumina of fly ash and part of calcium hydroxide, and (ii) CSH, by hydration of silica contained in fly ash and residual lime, was observed within both the reacting systems. For the FGD gypsum-based mixture, the conversion toward ettringite and CSH was highest at 70°C and increased with curing time. Some discrepancies in the hydration behavior between the mixtures were ascribed to differences in mineralogical composition between natural and FGD gypsum.

Flue gas desulfurization gypsum and coal fly ash as basic components of prefabricated building materials

TELESCA, ANTONIO;MARROCCOLI, Milena;CALABRESE, DANIELA;VALENTI, Gian Lorenzo;
2013

Abstract

The manufacture of prefabricated building materials containing binding products such as ettringite (6CaO•Al2O3•3SO3•32H2O) and calcium silicate hydrate (CSH) can give, in addition to other well-defined industrial activities, the opportunity of using wastes and by-products as raw materials, thus contributing to further saving of natural resources and protection of the environment. Two ternary mixtures, composed by 40% flue gas desulfurization (FGD) gypsum or natural gypsum (as a reference material), 35% calcium hydroxide and 25% coal fly ash, were submitted to laboratory hydrothermal treatments carried out within time and temperature ranges of 2 hours–7 days and 55°-85°C, respectively. The formation of (i) ettringite, by hydration of calcium sulfate given by FGD or natural gypsum, alumina of fly ash and part of calcium hydroxide, and (ii) CSH, by hydration of silica contained in fly ash and residual lime, was observed within both the reacting systems. For the FGD gypsum-based mixture, the conversion toward ettringite and CSH was highest at 70°C and increased with curing time. Some discrepancies in the hydration behavior between the mixtures were ascribed to differences in mineralogical composition between natural and FGD gypsum.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11563/35809
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 95
  • ???jsp.display-item.citation.isi??? 87
social impact