Extraction methods and their influence on yield when extracting thermo-vacuum-modified chestnut wood

Improvements in the yield and solubility of chestnut wood extractives, by using different extraction methods and molybdenum catalysts as support, have rarely been reported in literature. Many studies focus on the different parts of trees, except for the chemical characteristics of the remaining extractives achieved from thermally modified (THM) chestnut (Castanea sativa Mill) wood. This research seeks to better understand the effects of extraction techniques and catalysts on the yield and solubility of extractives. GC-MS analysis of the chloroform soluble and insoluble fractions was also used. Accelerated Solvent Extraction (ASE) 110◦C, Soxhlet, and autoclave extraction techniques were used to obtain extractives from untreated and thermally modified (THM) chestnut wood (170◦C for 3 h). Ethanol/H2O, ethanol/toluene, and water were the solvents used for each technique. A polyoxometalate compound (H3PMo12O40 ) and MoO3 supported on silica were used as catalysts. The THM induced a change in the wood’s surface color (∆E = 21.5) and an increase in mass loss (5.9%), while the equilibrium moisture content (EMC) was reduced by 17.4% compared to the control wood. The yields of the extractives and their solubility were always higher in THM and mainly used ASE as the technique. GC-MS analysis of the extractives, without catalyst support, showed different results for each extraction technique and type of wood (untreated and THM). Ultimately, the amount of extractive compound dissolved in each solvent will differ, and the choice of extraction technique will depend on the intended final application of the extracted chemical product.