Ordinary Portland cement (OPC) manufacture determines about 8% of the global anthropogenic CO2 emissions. This has led to both the cement producers and the scientific community to develop new cementitious materials with a reduced carbon footprint. Calcium sulfoaluminate (CSA) cements are special hydraulic binders from non-Portland clinkers; they represent an important alternative to OPC due to their peculiar composition and significantly lower impact on the environment. CSA cements contain less limestone and require lower synthesis temperatures, which means a reduced kiln thermal energy demand and lower CO2 emissions. CSA cements can also be mixed with supplementary cementitious materials (SCMs) which further reduce the carbon footprint. This article was aimed at evaluating the possibility of using different amounts (20 and 35% by mass) of water potabilization sludges (WPSs) as SCM in CSA-blended cements. WPSs were treated thermally (TT) at 700° in order to obtain an industrial pozzolanic material. The hydration properties and the technical behavior of two different CSA-blended cements were investigated using differential thermal–thermogravimetric and X-ray diffraction analyses, mercury intrusion porosimetry, shrinkage/expansion and compressive strength measurements. The results showed that CSA binders containing 20% by mass of TTWPSs exhibited technological properties similar to those relating to plain CSA cement and were characterized by more pronounced ecofriendly features.

Use of Potabilized Water Sludge in the Production of Low-Energy Blended Calcium Sulfoaluminate Cements

Antonio Telesca
Writing – Review & Editing
;
Neluta Ibris
Formal Analysis
;
Milena Marroccoli
Writing – Review & Editing
2021-01-01

Abstract

Ordinary Portland cement (OPC) manufacture determines about 8% of the global anthropogenic CO2 emissions. This has led to both the cement producers and the scientific community to develop new cementitious materials with a reduced carbon footprint. Calcium sulfoaluminate (CSA) cements are special hydraulic binders from non-Portland clinkers; they represent an important alternative to OPC due to their peculiar composition and significantly lower impact on the environment. CSA cements contain less limestone and require lower synthesis temperatures, which means a reduced kiln thermal energy demand and lower CO2 emissions. CSA cements can also be mixed with supplementary cementitious materials (SCMs) which further reduce the carbon footprint. This article was aimed at evaluating the possibility of using different amounts (20 and 35% by mass) of water potabilization sludges (WPSs) as SCM in CSA-blended cements. WPSs were treated thermally (TT) at 700° in order to obtain an industrial pozzolanic material. The hydration properties and the technical behavior of two different CSA-blended cements were investigated using differential thermal–thermogravimetric and X-ray diffraction analyses, mercury intrusion porosimetry, shrinkage/expansion and compressive strength measurements. The results showed that CSA binders containing 20% by mass of TTWPSs exhibited technological properties similar to those relating to plain CSA cement and were characterized by more pronounced ecofriendly features.
2021
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11563/147446
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 4
social impact