“Potential application of coal-fuel oil ash for the manufacture of building materials”

In this paper coal–fuel oil ash has been characterized in terms of leaching behaviour and reactivity against lime and gypsum in hydratory systems for the manufacture of building materials. Its behaviour was also compared to that of coal ash. Metal release was measured in a dynamic leaching test with duration up to 16 days. The results have shown that coal–fuel oil ash behaves very similarly to coal ash. The reactivity of coal–fuel oil ash against lime and gypsum was measured in mixtures containing only lime and in mixtures containing both lime and gypsum. These systems were hydrated at 25 and 40 ◦C under 100% R.H. The results have shown that the main hydration products are the same as those that are usually formed in similar coal ash-based systems. That is, calcium silicate hydrate in coal–fuel oil ash/lime systems and calcium silicate hydrate plus calcium trisulphoaluminate hydrate in coal–fuel oil ash/lime/gypsum systems. From the quantitative point of view, hydration runs showed that the amounts of both chemically combined water and reacted lime measured in the case under investigation are very similar to those found in similar coal ash-based systems. Finally, the measurement of unconfined compressive strength proved that the systems have potentiality for the manufacture of pre-formed building blocks.